Fabricating method for natural cellulose fiber blended with nano silver

ABSTRACT

The present invention provides a fabricating method for natural cellulose fiber blended with nano silver. 
     The fabricating method comprises following steps:
         Firstly, prepare nano silver colloidal sol by reduction titration for mixture of polyvinyl alcohol (PVA), silver nitrate (AgNO 3 ) and sodium borohydride (NaBH 4 ).   Secondly, prepare mixing cellulose serum by blending agitation for mixture of wood pulp, N-methylmorpholine N-oxide (NMMO) and stabilizer.   Thirdly, produce spinning dope by blending and dehydrating the nano silver colloidal sol and mixing cellulose serum.   Fourthly, produce fibrous tow by Dry-Jet Wet Spinning method in association with coagulation, regeneration in coagulation bath, and water rinse.   Finally, obtain final product of natural cellulose fiber blended with nano silver by post treatments of dry, oil and coil in proper order.

FIELD OF THE PRESENT INVENTION

The present invention relates to a fabricating method for natural cellulose fiber blended with nano silver, particularly for one belonging to eco-friendly process in producing non-woven from natural cellulose, whose process comprises following steps in proper order: prepare nano silver colloidal sol, prepare mixing cellulose serum, produce spinning dope, produce fibrous tow and obtain final product of natural cellulose fiber blended with nano silver by post treatments of dry, oil and coil in proper order.

BACKGROUND OF THE INVENTION

The techniques available for fabricating chemical fiber by blending nano silver colloidal sol with polymer fiber are disclosed as in Mainland China Patent Applications in filed numbers of 200410062799.3, 200510070895.7, 201010230063.8, 201010285121.7 and 201310523647.8 et cetera,. However, the wastes from spent chemical fiber of blending nano silver colloidal sol with polymer fiber aforesaid not only cause tremendous impact and burden to the environment but also discharge harmful drained materials because they are not biodegradable. Moreover, the antibacterial and sterilization abilities for the chemical fiber of blending nano silver colloidal sol with polymer fiber aforesaid are dispersedly divergent beyond processed control, which can not meet precise requirement of industrial application. Therefore, how to produce a natural cellulose fiber blended with nano silver having uniform and consistent antibacterial, sterilization and anti-static-electricity abilities and biodegradable features under precisely manufacturing parameters becomes critical and impending issue for the industry, which is also the target of our present invention.

SUMMARY OF THE INVENTION

The primary object of the present invention is to provide a fabricating method for natural cellulose fiber blended with nano silver comprising following steps:

Firstly, prepare nano silver colloidal sol by reduction titration for mixture of polyvinyl alcohol (PVA), silver nitrate (AgNO₃) and sodium borohydride (NaBH₄).

Secondly, prepare mixing cellulose serum by blending agitation for mixture of wood pulp, N-methylmorpholine N-oxide (NMMO) and stabilizer.

Thirdly, produce spinning dope by blending and dehydrating the nano silver colloidal sol and mixing cellulose serum.

Fourthly, produce fibrous tow by Dry-Jet Wet Spinning method in association with coagulation, regeneration in coagulation bath, and water rinse.

Finally, obtain final product of natural cellulose fiber blended with nano silver by post treatments of dry, oil and coil in proper order.

With foregoing process steps, by means of controlling the particle size and concentration of the nano silver colloidal sol, obtained natural cellulose fiber blended with nano silver will has good antibacterial capability, which is not only meet the precise requirement of uniform and consistent antibacterial and sterilization from industrial application but also effectively inhibit and eradicate the proliferation and growth of the microorganism including bacteria, mold or fungus so that it is beneficial to promote healthful, clean and comfortable life because the disease spread is practically controlled in consequence of the prevention from bacterial cross infection.

The other object of the present invention is to provide a fabricating method for natural cellulose fiber blended with nano silver to produce a final product of natural cellulose fiber blended with nano silver with antistatic and biodegradeable features. With antistatic feature, the natural cellulose fiber blended with nano silver of the present invention effectively avoids negative impact to the human physiological blood circulation, immune system and nervous system from static effect during wearing and taking-off clothes in winter season. Whereas, with biodegradeable feature, the natural cellulose fiber blended with nano silver of the present invention, the tremendous impact and burden to the environment caused by the wastes from spent conventional chemical fiber counterparts can be totally eradicated.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a flow chart of block diagram showing the fabricating process for the exemplary embodiment of the present invention.

FIG. 2 is a chemical structure of the Polyvinyl Alcohol (PVA) used in the present invention.

FIG. 3 is a chemical structure of the N-methylmorpholine N-oxide (NMMO) solvent used in the present invention.

FIG. 4 is a chemical structure of the pulp cellulose used in the present invention.

FIG. 5 is a distribution chart of suspended particle size for nano silver colloidal sol of 1000 ppm used in the present invention.

FIG. 6 is a Transmission Electron Microscopic graph (TEM) for nano silver colloidal sol of 100 times dilution used in the present invention.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

For further disclosing the fabricating process and effects of the present invention, following preferred exemplary embodiments in associated figures are detailed presented as below.

Please refer to FIGS. 1 to 4, the “fabricating method for natural cellulose fiber blended with nano silver” of the present invention comprises following steps:

(a) Put partially alkalized polyvinyl alcohol (PVA) power together with silver nitrate (AgNO₃) solution as precursor thereof into pure water for agitating to form polyvinyl alcohol (PVA) solution in gel state such that the alkalization degree and the molecular weight of partially alkalized polyvinyl alcohol (PVA) power added is 86-89 mole % and 14,700-98,000 respectively while the weight percentage of polyvinyl alcohol (PVA) solution is 3-12 wt %, and the concentration of polyvinyl alcohol (PVA) solution is good enough to enclose and protect the micro silver particles formed therein because the polyvinyl alcohol (PVA) features in low polymerization degree and water-solubility at low temperature, and the silver nitrate (AgNO₃) solution is created by dissolving the silver nitrate (AgNO₃) crystal into pure water, as well as the chemical structure of the polyvinyl alcohol (PVA) used here is shown as in FIG. 2;

(b) Put sodium borohydride (NaBH₄) into the gel state polyvinyl alcohol (PVA) solution for reduction titration by agitating to form nano silver colloidal sol such that the reduction titration is performed by sodium borohydride (NaBH₄) with mole ratio in range of 1:4-1:8, titration speed in range of 5-15 ml/min, agitating frequency about 200 rpm, and titration time about 10 minutes, and the concentration of produced nano silver sol is in range of 500-20,000 ppm while the diameter of the nano silver particle is in range of 10-150 nm;

(c) Put the nano silver colloidal sol into a mixing cellulose serum of wood pulp raw material and N-methylmorpholine N-oxide (NMMO) solvent for blending process to prepare blending mucilage such that the blending process is performed by putting raw material of chipped wood pulp, solvent of N-methylmorpholine N-oxide (NMMO), and stabilizer together into an expansion dissolving tank with constant temperature in range of 60-80 degrees centigrade (° C.) for blending agitation, and in association of dehydration in a vacuum condensing equipment with vacuum about 933 micro-Pa. Wherein, the raw material wood pulp is a mixture of soft wood and hard wood with blending ratio thereof in range of 0:100-100:0, and the content of α-cellulose is over 85% while the polymerization degree for the cellulose of wood pulp thereof is in range of 500-1200, and the weight percentage for the nano silver sol in the prepared blending mucilage is in range of 5-35 wt % while the concentration of the nano silver particle therein is in range of 100-5000 ppm, as well as the chemical structures of the N-methylmorpholine N-oxide (NMMO) and pulp cellulose used here are shown as in FIGS. 3 and 4 respectively;

(d) Evaporate water contained in the blending mucilage of nano silver colloidal sol and natural cellulose of wood pulp to form spinning dope by heating via a Thin Film Evaporator (TFE) under vacuum in range of 939-926 micro-Pa, heating temperature in range of 80-130 degrees centigrade (° C.) to dehydrate water down to range of 5-13% in 5 minutes so that the wood cellulose is dissolved into spinning dope owing to following mechanism for the blending process to prepare blending mucilage in previous step c, wherein other than both phases of natural cellulose of wood pulp and nano silver sol in the blending mucilage being able mutually penetrate each other and tightly bond together due to mutual compatibility, the shearing actions caused by mechanical agitation in the expansion dissolving tank make it as structure of continuous phase such that not only the stability of the is enhanced in proportional to promotion of uniformization degree for both phases but also even distribution of the nano silver particle in the spinning dope is ensured definitely with parameters that the composition percentages for all constituents in the spinning dope as following: the percentage of water (H₂O) is in range of 9-18%, the percentage of N-methylmorpholine N-oxide (NMMO) is in range of 75-87%, and the percentage of cellulose is in range of 6-11%;

(e) Spin the spinning dope via “Dry-Jet Wet Spinning Method” by means of conveying the spinning dope via boosted pressure to a continuous polymer filter (CPF) for filtration and defoaming treatment, feeding the spinning dope into a spinning block for extruding out as melt trickle via spinnerets therein, and thinning the melt trickle into fibrous tow by stretching it through an air gap to form bundle of fibrous tow;

(f) Feed the air cured fibrous tow into coagulation bath for coagulation, regeneration in coagulation liquid therein, and water rinse to form spinning filaments such that the concentration of the coagulation liquid is in range of 4.5-8.0%, and the residual quantity percentage of the N-methylmorpholine N-oxide (NMMO) solvent is less than 0.1% while the residual quantity percentage of the polyvinyl alcohol (PVA) solution is less than 0.3%; and

(g) Treat the spinning filaments with dry, oil and coil in proper order to produce final product of natural cellulose fiber blended with nano silver.

In previous step f, the residual polyvinyl alcohol (PVA) solution and residual N-methylmorpholine N-oxide (NMMO) solvent after coagulation, regeneration and water rinse should be further treated.

For separating out polyvinyl alcohol (PVA) solution, the process is performed in following steps: firstly, feed the initial residual polyvinyl alcohol (PVA) solution into a chromatography tank, and add glauber (Na₂SO₄) of 100 g/L together with borax (Na₂B₄O₇.10H₂O) of 16.7 g/L therein; secondly, add slight sodium carbonate (Na₂CO₃) therein to serve as pH modifier; and finally, the overall chemical reactions in the chromatography tank make the polyvinyl alcohol (PVA) solution be condensing, gelling and separating out so that the sorted polyvinyl alcohol (PVA) can be isolated from the N-methylmorpholine N-oxide (NMMO) solvent to avoid from affecting the recycling process of N-methylmorpholine N-oxide (NMMO) solvent.

For recycling N-methylmorpholine N-oxide (NMMO) solvent, the process is performed in following steps:

A. First Filtration:

Perform the first filtration for the initial residual N-methylmorpholine N-oxide (NMMO) solvent by means of pleated polypropylene (PP) filter cartridge of 1-20 μ;

B. Flocculation:

Put the treated N-methylmorpholine N-oxide (NMMO) solvent from previous first filtration together with flocculant and necessary additive of 1.5 mg/L into a flocculation tank for flocculation with duration for 1 hour such that colloidal impurities is aggregated into clumping while the insoluble impurities is coagulated into polymerized floc due to function of existing flocculant so that amassed clumping and floc will start sedimentation and discharge through filtering net.

C. Purification:

Feed the treated N-methylmorpholine N-oxide (NMMO) solvent from previous flocculation into a purification system for ion exchange for purification under pH value in range of 8-9 so that not only the color impurities is separated out but also the purification is enhanced.

D. Second Filtration:

Perform the second filtration for the treated N-methylmorpholine N-oxide (NMMO) solvent from previous purification by means of Ultra-filter (UF) and reverse osmosis (RO) filter; and

E. Condensation:

Perform the circulated condensation for the treated N-methylmorpholine N-oxide (NMMO) solvent from previous second filtration by circulation of multi-stage evaporation tank system so that not only the purity of the recycled N-methylmorpholine N-oxide (NMMO) solvent is enhanced up to 50.0˜78.0% but also the recycling rate thereof is promoted over 99.5%.

Thus, the recycled N-methylmorpholine N-oxide (NMMO) solvent is good enough to be reused in the fabricating process of the present invention

In order to further prove and justify foregoing features and practical effects, some preferred exemplary embodiments are described below.

First Exemplary Embodiment:

Put partially alkalized polyvinyl alcohol (PVA) power of 5.0 g and silver nitrate

(AgNO₃) solution of suitable quantity into pure water of 95.0 g to agitate for 2 hours to form polyvinyl alcohol (PVA) solution in gel state with 0.1 molar concentration (M) of 0.5 ml, and put sodium borohydride (NaBH₄) with 0.2 molar concentration (M) into the gel state polyvinyl alcohol (PVA) solution for reduction titration by agitating to obtain nano silver colloidal sol of 1000 ppm, wherein the color of the polyvinyl alcohol (PVA) gel will from initial translucent color gradually turn into yellow, light brown, deep brown and final dark brown upon end of the reduction titration. FIG. 5 is a distribution chart of suspended particle size for nano silver colloidal sol of 1000 ppm obtained from process aforesaid. According to analysis of the FIG. 5, the suspended particle size for nano silver colloidal sol of 1000 ppm mainly spreads in the range of 15-25 nm. Moreover,

FIG. 6 is a Transmission Electron Microscopic graph (TEM) for nano silver colloidal sol of 100 times dilution obtained from process aforesaid. According to illustration of the FIG. 6, it is apparent that the suspended particle size less than 100 nm can be obtained from foregoing process of the present invention.

Second Exemplary Embodiment: (Preparation for Samples 1-11)

Firstly, mix wood pulp for polymerization degree of cellulose in 650 with N-methylmorpholine N-oxide (NMMO) solvent to create a mixing cellulose serum, and add put a nano silver colloidal sol with weight percentage of 5-35 wt % into the mixing cellulose serum for blending process to prepare a blending mucilage with concentration of nano silver particle in range of 100-5000 ppm;

Secondly, evaporate water contained in the blending mucilage by heating via a Thin Film Evaporator (TFE) under heating temperature in range of 80-130 degrees centigrade (° C.) to dehydrate water down to range of 5-13% in 5 minutes to form a spinning dope with sample Composition for testing samples 1-11 of spinning dope as shown in the upper half portion of Table-1.

Thirdly, spin the spinning dope via “Dry-Jet Wet Spinning Method” by means of conveying the spinning dope via boosted pressure to a continuous polymer filter (CPF) for filtration and defoaming treatment, feeding the spinning dope into a spinning block for extruding out as melt trickle via spinnerets therein, and thinning the melt trickle into fibrous tow by stretching it through an air gap to form bundle of fibrous tow;

Finally, feed the air cured fibrous tow into coagulation bath for coagulation, regeneration in coagulation liquid therein, water rinse to form spinning filaments, and treat the spinning filaments with dry, oil and coil in proper order to produce final product of natural cellulose fiber blended with nano silver having antibacterial capability, which is tabulated in the upper half portion of Table-1 to show the sample composition for testing samples of spinning dope for samples 1-11.

Third Exemplary Embodiment: (Preparation for Samples 12-22)

Firstly, mix wood pulp for polymerization degree of cellulose in 1050 with N-methylmorpholine N-oxide (NMMO) solvent to create a mixing cellulose serum, and add put a nano silver colloidal sol with weight percentage of 5-35 wt % into the mixing cellulose serum for blending process to prepare a blending mucilage with concentration of nano silver particle in range of 100-5000 ppm;

Secondly, evaporate water contained in the blending mucilage by heating via a Thin Film Evaporator (TFE) under heating temperature in range of 80-130 degrees centigrade (° C.) to dehydrate water down to range of 5-13% in 5 minutes to form a spinning dope with sample Composition for testing samples 12-22 of spinning dope as shown in the lower half portion of Table-1;

Thirdly, spin the spinning dope via “Dry-Jet Wet Spinning Method” by means of conveying the spinning dope via boosted pressure to a continuous polymer filter (CPF) for filtration and defoaming treatment, feeding the spinning dope into a spinning block for extruding out as melt trickle via spinnerets therein, and thinning the melt trickle into fibrous tow by stretching it through an air gap to form bundle of fibrous tow;

Finally, feed the air cured fibrous tow into coagulation bath for coagulation, regeneration in coagulation liquid therein, water rinse to form spinning filaments, and treat the spinning filaments with dry, oil and coil in proper order to produce final product of natural cellulose fiber blended with nano silver having antibacterial capability, which is tabulated in the lower half portion of Table-1 to show the sample composition for testing samples of spinning dope for samples 12-22.

TABLE 1 Sample Composition for testing samples of spinning dope BRSS CNSP CCBS SCBS MCBS Sample PMDC (wt %) (ppm) (%) (%) (%) :[Exemplary Embodiment - 2: for samples 1-11]: 1 650 5 100 11.2 77.2 11.6 2 650 8 500 11.1 77.5 11.4 3 650 11 1000 12.3 77.1 10.6 4 650 14 1500 11.6 77.4 11.0 5 650 17 2000 11.4 77.5 11.1 6 650 20 2500 11.4 77.1 11.5 7 650 23 3000 11.3 77.7 11.0 8 650 26 3500 12.0 77.5 10.5 9 650 29 4000 11.4 77.4 11.2 10 650 32 4500 11.4 78.3 10.3 11 650 35 5000 11.7 78.2 10.1 :[Exemplary Embodiment - 3: for samples 12-22]: 12 1050 5 100 11.6 77.7 10.7 13 1050 8 500 11.3 77.0 11.7 14 1050 11 1000 11.2 78.2 10.6 15 1050 14 1500 11.4 77.5 11.1 16 1050 17 2000 11.7 77.3 11.0 17 1050 20 2500 11.3 78.3 10.4 18 1050 23 3000 12.0 75.9 12.1 19 1050 26 3500 11.9 77.3 10.8 20 1050 29 4000 11.5 78.0 10.5 21 1050 32 4500 12.1 76.1 11.8 22 1050 35 5000 11.7 77.6 10.7 Notation PMDC denotes to polymerization degree of cellulose BRSS denotes to blending ratio of nano silver sol CNSP denotes to concentration of nano silver particles CCBS denotes to cellulose content in blending solution SCBS denotes to solvent content in blending solution MCBS denotes to moisture content in blending solution

Fourth Exemplary Embodiment: (Assessment for Antibacterial Capability)

Testing Bacterial Strains:

Adopt type (A) bacteria: Methicillin Resistant Staphyloccous Aureus (MRSA) (ATCC 6538P) and type (B) bacteria: Klebsiella Pheumoniae (ATCC 4352) as two experiment bacterial strains.

Principle:

In a nano silver sol, which is a colloidal suspension of very small solid nano silver particles in a continuous liquid medium, the solid nano silver particles are charged with anions while the bacterial cell membranes of the testing bacterial strains are charged with cations. A Dehydrogenase-Superantigen (SAg) structure is created when both the solid nano silver particles with anions and bacterial cell membranes of the testing bacterial strains with cations are chemically combined together. Thereby, the bacterial cell membranes of the testing bacterial strains will gradually fade away and become perforation with results that massive drainage of reduction sugar, protein and potassium ions is caused, as well as membrane potential thereof and Adenosine triphosphate (ATP) are exhausted because the solid nano silver particles in the testing bacterial strains can spoil bacterial activity and DNA, interrupt bacterial signal transmission and further inhibit growth of the testing bacterial strains. Finally, the testing bacterial strains will die because they are neither to breathe and metabolism nor reproduction.

Testing Object:

Take subject natural cellulose fiber blended with nano silver of the present invention as antibacterial sample to determine the degree of antibacterial capability respectively.

Tables 2 and 3 list testing results in antibacterial capability for subject natural cellulose fiber blended with nano silver of the present invention.

Foundation:

The experiment is in accordance with JIS L1902-1998 Quantitative Method.

Testing Bacterial Strains:

Adopt type (A) bacteria: Methicillin Resistant Staphyloccous Aureus (MRSA) (ATCC 6538P) and type (B) bacteria: Klebsiella Pheumoniae (ATCC 4352) as two experiment bacterial strains.

Experiment:

The concentration of incubated testing bacterial strain (TBS) within 1.0±0.3E+5 (number/ml) means valid for the experiment.

-   Ma denotes bacteria number for testing bacterial strain (TBS) of     un-processed sample in immediate count upon cleansing without     incubation. -   Mb denotes bacteria number for testing bacterial strain (TBS) of     un-processed sample after being incubated for 18˜24 hours. -   Mc denotes bacteria number for testing bacterial strain (TBS) of     processed sample after being incubated for 18˜24 hours.

Calculating Formula:

The growing activity value of the testing bacterial strain (TBS) is denoted as “BGA”, which is calculated by following formula such that BGA>1.5 means valid of the experiment.

The upper half portion and lower half portion of Table-2 shows the antibacterial capability to the bacterial strains of Methicillin Resistant Staphyloccous Aureus (MRSA) (ATCC 6538P) for natural cellulose fiber blended with nano silver for samples 1-11 and 12-22 respectively while the upper half portion and lower half portion of Table-3 shows the antibacterial capability to the bacterial strains of Klebsiella Pheumoniae (ATCC 4352) for natural cellulose fiber blended with nano silver for samples 1-11 and 12-22 respectively, and all sample compositions in both of Table-2 and Table-3 are based on the first exemplary embodiment.

TABLE 2 Antibacterial capability for natural cellulose fiber blended with nano silver BRSS CNSP TSRT Sample PMDC (wt %) (ppm) ABCF SRCF (Yes/No) 1 650 5 100 >1.2 >1.5 No 2 650 8 500 >1.6 >2.0 No 3 650 11 1000 >2.1 >3.8 No 4 650 14 1500 >4.0 >4.1 Yes 5 650 17 2000 >4.7 >4.2 Yes 6 650 20 2500 >4.8 >4.2 Yes 7 650 23 3000 >5.6 >4.0 Yes 8 650 26 3500 >4.9 >4.6 Yes 9 650 29 4000 >5.1 >4.2 Yes 10 650 32 4500 >5.1 >4.3 Yes 11 650 35 5000 >5.2 >4.3 Yes 12 1050 5 100 >1.6 >1.7 No 13 1050 8 500 >1.7 >2.1 No 14 1050 11 1000 >2.2 >4.0 No 15 1050 14 1500 >4.1 >4.2 Yes 16 1050 17 2000 >4.8 >4.3 Yes 17 1050 20 2500 >5.0 >4.3 Yes 18 1050 23 3000 >4.9 >4.2 Yes 19 1050 26 3500 >5.1 >4.2 Yes 20 1050 29 4000 >4.9 >4.2 Yes 21 1050 32 4500 >5.1 >4.5 Yes 22 1050 35 5000 >5.0 >4.5 Yes Testing Method JIS L1902-1998 Quantitative Method Testing biological strains Methicillin Resistant Staphyloccous Aureus (MRSA) (ATCC 6538P) Notation PMDC denotes to polymerization degree of cellulose BRSS denotes to blending ratio of nano silver sol CNSP denotes to concentration of nano silver particles ABCF denotes to antibacterial value of natural cellulose fiber SRCF denotes to sterilization value of natural cellulose fiber TSRT denotes to testing results for (Yes/No) :[Interpretation]: The upper half portion and lower half portion of Table-2 shows the antibacterial capability to the bacterial strains of Methicillin Resistant Staphyloccous Aureus (MRSA) (ATCC 6538P) for natural cellulose fiber blended with nano silver for samples 1-11 and 12-22 respectively, and all sample compositions in the Table-2 are based on the first exemplary embodiment.

TABLE 3 Antibacterial capability for natural cellulose fiber blended with nano silver BRSS CNSP TSRT Sample PMDC (wt %) (ppm) ABCF SRCF (Yes/No) 1 650 5 100 >1.2 >1.5 No 2 650 8 500 >1.5 >2.0 No 3 650 11 1000 >2.3 >4.0 Yes 4 650 14 1500 >4.0 >4.0 Yes 5 650 17 2000 >4.7 >3.9 Yes 6 650 20 2500 >4.8 >4.2 Yes 7 650 23 3000 >4.8 >4.2 Yes 8 650 26 3500 >4.8 >4.3 Yes 9 650 29 4000 >5.0 >4.1 Yes 10 650 32 4500 >5.1 >4.1 Yes 11 650 35 5000 >5.1 >4.2 Yes 12 1050 5 100 >1.7 >1.8 No 13 1050 8 500 >1.6 >1.8 No 14 1050 11 1000 >2.3 >4.0 Yes 15 1050 14 1500 >4.2 >4.1 Yes 16 1050 17 2000 >4.9 >4.1 Yes 17 1050 20 2500 >5.1 >4.2 Yes 18 1050 23 3000 >4.7 >4.0 Yes 19 1050 26 3500 >4.9 >4.0 Yes 20 1050 29 4000 >5.1 >4.1 Yes 21 1050 32 4500 >5.1 >4.3 Yes 22 1050 35 5000 >5.0 >4.3 Yes Testing Method JIS L1902-1998 Quantitative Method Testing biological strains Klebsiella Pheumoniae (ATCC 4352) Notation PMDC denotes to polymerization degree of cellulose BRSS denotes to blending ratio of nano silver sol CNSP denotes to concentration of nano silver particles ABCF denotes to antibacterial value of natural cellulose fiber SRCF denotes to sterilization value of natural cellulose fiber TSRT denotes to testing results for (Yes/No) :[Interpretation]: The upper half portion and lower half portion of Table-3 shows the antibacterial capability to the bacterial strains of Klebsiella Pheumoniae (ATCC 4352) for natural cellulose fiber blended with nano silver for samples 1-11 and 12-22 respectively, and all sample compositions in the Table-3 are based on the first exemplary embodiment.

Tables-2 and 3 respectively show the antibacterial capability to the bacterial strains of Methicillin Resistant Staphyloccous Aureus (MRSA) (ATCC 6538P) and Klebsiella Pheumoniae (ATCC 4352) for natural cellulose fiber blended with nano silver for all samples 1-22. According to Tables 2 and 3, the subject natural cellulose fiber blended with nano silver of the present invention has good bacteriostatic and bactericidal effects to the testing bacterial strains of type (A) bacteria: Methicillin Resistant Staphyloccous Aureus (MRSA) (ATCC 6538P) and type (B) bacteria: Klebsiella Pheumoniae (ATCC 4352).

Fifth Exemplary Embodiment:

(Assessment for Antibacterial capability after i0 times of water laundering)

The experimental results in antibacterial capability for all samples of natural cellulose fiber blended with nano silver are listed in Table 4, wherein each sample has been treated with 10 times of water laundering in 70 degrees centigrade (70° C.) hot water with 5 grams per liter (5 g/L) detergent for 45 minutes.

TABLE 4 Antibacterial capability for natural cellulose fiber blended with nano silver after i0 times of water laundering BRSS CNSP TSRT Sample PMDC (wt %) (ppm) ABCF SRCF (Yes/No) 1 650 5 100 >1.2 >1.5 No 2 650 8 500 >1.5 >1.7 No 3 650 11 1000 >2.0 >3.6 No 4 650 14 1500 >4.6 >4.1 Yes 5 650 17 2000 >4.8 >4.1 Yes 6 650 20 2500 >4.9 >4.1 Yes 7 650 23 3000 >4.9 >4.1 No 8 650 26 3500 >4.8 >4.2 Yes 9 650 29 4000 >4.9 >4.0 Yes 10 650 32 4500 >5.0 >4.2 Yes 11 650 35 5000 >4.8 >4.1 Yes 12 1050 5 100 >1.6 >1.6 No 13 1050 8 500 >1.7 >1.8 No 14 1050 11 1000 >1.9 >3.4 No 15 1050 14 1500 >4.2 >3.6 Yes 16 1050 17 2000 >4.9 >4.0 Yes 17 1050 20 2500 >4.9 >4.0 Yes 18 1050 23 3000 >4.9 >4.0 Yes 19 1050 26 3500 >4.8 >4.0 Yes 20 1050 29 4000 >4.8 >4.1 Yes 21 1050 32 4500 >5.0 >4.0 Yes 22 1050 35 5000 >5.1 >4.1 Yes Testing Method JIS L1902-1998 Quantitative Method Testing biological strains Klebsiella Pheumoniae (ATCC 4352) Notation PMDC denotes to polymerization degree of cellulose BRSS denotes to blending ratio of nano silver sol CNSP denotes to concentration of nano silver particles ABCF denotes to antibacterial value of natural cellulose fiber SRCF denotes to sterilization value of natural cellulose fiber TSRT denotes to testing results for (Yes/No) :[Interpretation]: The upper half portion and lower half portion of Table-4 shows the antibacterial capability for natural cellulose fiber blended with nano silver after i0 times of water laundering for samples 1-11 and 12-22 respectively, and all sample compositions in the Table-4 are based on the first exemplary embodiment.

Tables-2 and 3 respectively show the antibacterial capability to the bacterial strains of Methicillin Resistant Staphyloccous Aureus (MRSA) (ATCC 6538P) and Klebsiella Pheumoniae (ATCC 4352) for natural cellulose fiber blended with nano silver for all samples 1-22. According to Tables 2 and 3, the subject natural cellulose fiber blended with nano silver of the present invention has good bactericidal effects if the concentration of nano silver particles (CNSP) reaches 100 ppm, and has excellent bacteriostatic effects if the concentration of nano silver particles (CNSP) reaches 1500 ppm, which proves and justifies that the subject natural cellulose fiber blended with nano silver of the present invention can definitely be modified to reach a level to have good antibacterial capability.

Table-4 shows that the antibacterial capability for natural cellulose fiber blended with nano silver after i0 times of hot water laundering with detergent put therein for all samples 1-122 remains over 90% antibacterial capability as original antibacterial capability before water laundering, which proves and justifies that the subject natural cellulose fiber blended with nano silver of the present invention has better long-lasting antibacterial capability than conventional counterparts available in the market, which is either treated with different surfactants or added with various additives.

Sixth Exemplary Embodiment: (Assessment for Antistatic Capability)

The assessment in antistatic capability for all samples of natural cellulose fiber blended with nano silver is performed criteria of “Specified Requirements of Antistatic Textiles” (FTTS-FA-009) from “Committee for Conformity Assessment of Accreditation and Certification on Functional and Technical Textiles” in the Republic of China (www.ftts.org.tw) and specification of “Electrical Surface Resistivity of Fabrics” (AATCC76) from American Association of Textile Chemists and Colorists (AATCC), wherein each sample has been tested with surface resistivity via concentric electrode to determine the degree of antistatic capability respectively.

TABLE 5 Antistatic capability for natural cellulose fiber blended with nano silver SRCF TSRT Sample PMDC BRSS (wt %) CNSP (ppm) (Ω) (Grade) 1 650 5 100  6.44 × 10¹⁰ 1 2 650 8 500 1.32 × 10⁹ 2 3 650 11 1000 2.05 × 10⁹ 2 4 650 14 1500 2.66 × 10⁹ 2 5 650 17 2000 4.32 × 10⁹ 2 6 650 20 2500 6.54 × 10⁹ 2 7 650 23 3000 8.02 × 10⁹ 2 8 650 26 3500 9.78 × 10⁹ 2 9 650 29 4000 1.02 × 10⁸ 2 10 650 32 4500 3.24 × 10⁸ 2 11 650 35 5000 5.25 × 10⁸ 2 12 1050 5 100  8.64 × 10¹⁰ 1 13 1050 8 500 2.22 × 10⁹ 2 14 1050 11 1000 2.30 × 10⁹ 2 15 1050 14 1500 3.56 × 10⁹ 2 16 1050 17 2000 6.82 × 10⁹ 2 17 1050 20 2500 7.04 × 10⁹ 2 18 1050 23 3000 7.99 × 10⁹ 2 19 1050 26 3500 8.98 × 10⁹ 2 20 1050 29 4000 1.69 × 10⁸ 2 21 1050 32 4500 4.54 × 10⁸ 2 22 1050 35 5000 5.88 × 10⁸ 2 Notation PMDC denotes to polymerization degree of cellulose BRSS denotes to blending ratio of nano silver sol CNSP denotes to concentration of nano silver particles SRCF denotes to surface resistivity of natural cellulose fiber TSRT denotes to testing results for (Rating Grade) :[Interpretation]: The upper half portion and lower half portion of Table-5 shows the antistatic capability for natural cellulose fiber blended with nano silver for samples 1-11 and 12-22 respectively, and all sample compositions in the Table-5 are based on the first exemplary embodiment.

Table-5 shows that the rating grades for testing results (TSRT) in the antistatic capability for natural cellulose fiber blended with nano silver for all samples 1-22 become “grade 2” if the concentration of nano silver particles (CNSP) is over 100 ppm, which means the subject natural cellulose fiber blended with nano silver of the present invention certainly has good antistatic capability. Moreover, Table-5 also shows that the surface resistivity (SRCF) in natural cellulose fiber blended with nano silver for all samples 1-22 proportionally increases to the concentration of nano silver particles (CNSP), which proves and justifies that the subject natural cellulose fiber blended with nano silver of the present invention has better antistatic capability than conventional counterparts available in the market.

Conclusion of the foregoing disclosure heretofore, the subject natural cellulose fiber blended with nano silver of the present invention certainly has good antibacterial capability, which is not only meet the precise requirement of uniform and consistent antibacterial and sterilization from industrial application but also effectively inhibit and eradicate the proliferation and growth of the microorganism including bacteria, mold or fungus so that it is beneficial to promote healthful, clean and comfortable life because the disease spread is practically controlled in consequence of the prevention from bacterial cross infection. Moreover, the subject natural cellulose fiber blended with nano silver of the present invention certainly also has good antistatic capability, which effectively avoid negative impact to the human physiological blood circulation, immune system and nervous system from static effect during wearing and taking-off clothes in winter season. More notably, the subject natural cellulose fiber blended with nano silver of the present invention certainly also has good biodegradable capability since it is fabricated from natural cellulose of wood pulp so that the tremendous impact and burden to the environment caused by the wastes from spent conventional chemical fiber counterparts can be totally eradicated. Accordingly, the subject natural cellulose fiber blended with nano silver of the present invention meet novelty and practical usage in industry of patentable criterion. Therefore, we submit the patent application for the present invention in accordance with related patent laws for your perusal. 

What is claimed is:
 1. A fabricating method for natural cellulose fiber blended with nano silver comprises following steps: (a) Put partially alkalized polyvinyl alcohol (PVA) power together with silver nitrate (AgNO₃) solution as precursor thereof into pure water for agitating to form polyvinyl alcohol (PVA) solution in gel state such that the alkalization degree and the molecular weight of partially alkalized polyvinyl alcohol (PVA) power added is 86-89 mole % and 14,700-98,000 respectively while the weight percentage of polyvinyl alcohol (PVA) solution is 3-12 wt %, and the concentration of polyvinyl alcohol (PVA) solution is good enough to enclose and protect the micro silver particles formed therein because the polyvinyl alcohol (PVA) features in low polymerization degree and water-solubility at low temperature, and the silver nitrate (AgNO₃) solution is created by dissolving the silver nitrate (AgNO₃) crystal into pure water; (b) Put sodium borohydride (NaBH₄) into the gel state polyvinyl alcohol (PVA) solution for reduction titration by agitating to form nano silver colloidal sol such that the reduction titration is performed by sodium borohydride (NaBH₄) with mole ratio in range of 1:4-1:8, titration speed in range of 5-15 ml/min, agitating frequency about 200 rpm, and titration time about 10 minutes, and the concentration of produced nano silver sol is in range of 500-20,000 ppm while the diameter of the nano silver particle is in range of 10-150 nm; (c) Put the nano silver colloidal sol into a mixing cellulose serum of wood pulp raw material and N-methylmorpholine N-oxide (NMMO) solvent for blending process to prepare blending mucilage such that the blending process is performed by putting raw material of chipped wood pulp, solvent of N-methylmorpholine N-oxide (NMMO), and stabilizer together into an expansion dissolving tank with constant temperature in range of 60-80 degrees centigrade (° C.) for blending agitation, and in association of dehydration in a vacuum condensing equipment with vacuum about 933 micro-Pa. such that the content of α-cellulose is over 85% while the polymerization degree for the cellulose of wood pulp is in range of 500-1200, and the weight percentage for the nano silver sol in the prepared blending mucilage is in range of 5-35 wt % while the concentration of the nano silver particle therein is in range of 100-5000 ppm; (d) Evaporate water contained in the blending mucilage of nano silver colloidal sol and natural cellulose of wood pulp to form spinning dope by heating via a Thin Film Evaporator (TFE) under vacuum in range of 939-926 micro-Pa, heating temperature in range of 80-130 degrees centigrade (° C.) to dehydrate water down to range of 5-13% in 5 minutes so that the wood cellulose is dissolved into spinning dope with the composition percentages for all constituents in the spinning dope are as following: the percentage of water (H₂O) is in range of 9-18%, the percentage of N-methylmorpholine N-oxide (NMMO) is in range of 75-87%, and the percentage of cellulose is in range of 6-11%; (e) Spin the spinning dope via “Dry-Jet Wet Spinning Method” by means of conveying the spinning dope via boosted pressure to a continuous polymer filter (CPF) for filtration and defoaming treatment, feeding the spinning dope into a spinning block for extruding out as melt trickle via spinnerets therein, and thinning the melt trickle into fibrous tow by stretching it through an air gap to form bundle of fibrous tow; (f) Feed the air cured fibrous tow into coagulation bath for coagulation, regeneration in coagulation liquid therein, and water rinse to form spinning filaments such that the concentration of the coagulation liquid is in range of 4.5-8.0%, and the residual quantity percentage of the N-methylmorpholine N-oxide (NMMO) solvent is less than 0.1% while the residual quantity percentage of the polyvinyl alcohol (PVA) solution is less than 0.3%; and (g) Treat the spinning filaments with dry, oil and coil in proper order to produce final product of natural cellulose fiber blended with nano silver.
 2. The “fabricating method for natural cellulose fiber blended with nano silver” as recited in claim 1, wherein the raw material wood pulp used in the step c is a mixture of soft wood and hard wood with blending ratio thereof in range of 0:100-100:0, and the polymerization degree for the cellulose of wood pulp thereof is in range of 500-1200 while the content of α-cellulose is over 85%.
 3. The “fabricating method for natural cellulose fiber blended with nano silver” as recited in claim 1, wherein the raw material wood pulp used in the step c is a soft wood, whose polymerization degree for the cellulose of wood pulp is in range of 500-1200 while the content of α-cellulose is over 85%.
 4. The “fabricating method for natural cellulose fiber blended with nano silver” as recited in claim 1, wherein the raw material wood pulp used in the step c is a hard wood, whose polymerization degree for the cellulose of wood pulp is in range of 500-1200 while the content of α-cellulose is over 85%.
 5. The “fabricating method for natural cellulose fiber blended with nano silver” as recited in claim 1, wherein the residual polyvinyl alcohol (PVA) solution after coagulation, regeneration and water rinse in step f is further treated for separating out polyvinyl alcohol (PVA) by means of process performed in following steps: firstly, feed the initial residual polyvinyl alcohol (PVA) solution into a chromatography tank, and add glauber (Na2SO4) of 100 g/L together with borax (Na2B407- 10H20) of 16.7 g/L therein, secondly add slight sodium carbonate (Na2CO3) therein to serve as pH modifier, and finally, the overall chemical reactions in the chromatography tank make the polyvinyl alcohol (PVA) solution be condensing, gelling and separating out so that the sorted polyvinyl alcohol (PVA) can be isolated from the N-methylmorpholine N-oxide (NMMO) solvent to avoid from affecting the recycling process of N-methylmorpholine N-oxide (NMMO) solvent.
 6. The “fabricating method for natural cellulose fiber blended with nano silver” as recited in claim 1, wherein in step f, the residual N-methylmorpholine N-oxide (NMMO) solvent after coagulation, regeneration and water rinse is further treated for recycling N-methylmorpholine N-oxide (NMMO) solvent such that the process is performed in following steps: A. First Filtration: Perform the first filtration for the initial residual N-methylmorpholine N-oxide (NMMO) solvent by means of pleated polypropylene (PP) filter cartridge of 1-20 μ; B. Flocculation: Put the treated N-methylmorpholine N-oxide (NMMO) solvent from previous first filtration together with flocculant and necessary additive of 1.5 mg/L into a flocculation tank for flocculation with duration for 1 hour such that colloidal impurities is aggregated into clumping while the insoluble impurities is coagulated into polymerized floc due to function of existing flocculant so that amassed clumping and floc will start sedimentation and discharge through filtering net; C. Purification: Feed the treated N-methylmorpholine N-oxide (NMMO) solvent from previous flocculation into a purification system for ion exchange for purification under pH value in range of 8-9 so that not only the color impurities is separated out but also the purification is enhanced; D. Second Filtration: Perform the second filtration for the treated N-methylmorpholine N-oxide (NMMO) solvent from previous purification by means of Ultra-filter (UF) and reverse osmosis (RO) filter; and E. Condensation: Perform the circulated condensation for the treated N-methylmorpholine N-oxide (NMMO) solvent from previous second filtration by circulation of multi-stage evaporation tank system so that not only the purity of the recycled N-methylmorpholine N-oxide (NMMO) solvent is enhanced up to 50.0˜78.0% but also the recycling rate thereof is promoted over 99.5%. 